16MNCR5
16MNCR5 Grade Introduction:
16MnCr5 steel is alloyed case hardening engineering steels for parts that require core tensile strength of 800 – 1100 N/mm² and good wearing resistance. It is an engineering material typically used to manufacture piston bolts, camshafts, levers, and other vehicle and mechanical engineering components. 16MNCR5 Grade is also available in different shapes like Round, Flat, Square steel Bars.
16MNCR5 Grade Application:
- Gearings in rotating machinery
- Valve bodies
- Pumps
- Fittings
- High-load wheels
- Bolts and double-headed bolts
- Gears
- Internal combustion engines
- Machine tools
16MNCR5 Equivalent Grades:
Standard |
ASTM A29/A29M |
DIN EN 10083/3 |
JIS G4053 |
DIN/T DIN17210 |
16MNCR5 Chemical Composition:
Element |
C |
Si |
Mn |
P |
S |
Cr |
Content (%) |
0.14-0.19 |
≤0.40 |
1.00~1.30 |
≤0.035 |
≤0.035 |
0.80~1.10 |
Mechanical Properties:
Property |
Tensile (MPa) |
Yield (MPa) |
Bulk Modulus (GPa) |
Shear Modulus (GPa) |
Poisson’s Ratio |
Thermal Conductivity (W/mK) |
Value |
520 |
415 Min |
140 |
80 |
0.27-0.30 |
46.6 |
Physical Properties:
Quantity |
Value |
Unit |
Thermal Expansion |
10 – 10 |
e-6/K |
Thermal Conductivity |
25 – 25 |
W/m.K |
Specific Heat |
460 – 460 |
J/kg.K |
Melting Temperature |
1450 – 1510 |
°C |
Density |
7700 – 7700 |
kg/m3 |
Resistivity |
0.55 – 0.55 |
Ohm.mm2/m |
Thermal Properties:
Quantity |
Value |
Unit |
Thermal Expansion |
10 – 10 |
e-6/K |
Thermal Conductivity |
25 – 25 |
W/m.K |
Forging Properties:
Hot forming temperature: 1100-850°C.
Stress Relieving:
600-680°C